Removing steel studs from an aluminum head can lead to some serious consequences. Lets say that the head is 356 alloy (just as an example, a common casting alloy)

If it is well heat treated it can have a tensile strength of around 35,000 psi.

If it is not its tensile strength is around 25,000 psi or less.

Thats a drop of almost %29. Other higher strength alloys can drop by as much as %80.

At what temperature does this happen? About 750 F. Can't you get the heat treatment back? it could take from 60 min to 4 days at high temps to get it back to strength.

Aluminum is not like steel. Steel has well known color/temp relationship. Red hot means an exact temperature. "But I didnt heat it up that much" .... A "red hot" steel bolt is at over 1,200 F. Kiss your aluminum heat treatment good by.

So you have a stuck or broken plug or stud. You heat up the area (even just the threads) around it as much as you please. Hey, it came out. Then maybe a few months down the road you find the threads are falling apart when you take the part off again. Maybe new head time.

Steel melts at a much higher temp then aluminum. Steel gives a very good warning of when it will melt. Aluminum on the other hand will just slump. One second you are happy, the next the aluminum has melted with out warning and its really new head time.

Watch out when heating our expensive aluminum parts!

Pawling NY

Cars I have: 93 Eurovan MV 75 Westy 73 Super

Cars I had: 89 GTi 16v 87 Syncro 83 Rabbit GTi 82 Vanagon Diesel (w 83 GTi engine)


Back to: Top of message | Previous page | Main VANAGON page

Please note - During the past 17 years of operation, several gigabytes of Vanagon mail messages have been archived. Searching the entire collection will take up to five minutes to complete. Please be patient!


Return to the archives @ gerry.vanagon.com


The vanagon mailing list archives are copyright (c) 1994-2011, and may not be reproduced without the express written permission of the list administrators. Posting messages to this mailing list grants a license to the mailing list administrators to reproduce the message in a compilation, either printed or electronic. All compilations will be not-for-profit, with any excess proceeds going to the Vanagon mailing list.

Any profits from list compilations go exclusively towards the management and operation of the Vanagon mailing list and vanagon mailing list web site.